1010 Holzpellets
Preparation |
CEN 14780 |
total moisture |
CEN 14774-1 |
(inherent) moisture of analysis sample |
CEN 14774-3 |
Ash 550°C |
CEN 14775 |
Ash 815°C |
ISO 1171 |
volatile matter 900°C |
CEN 15148 |
total sulfur S |
CEN 15289 |
total carbon C (TC) |
CEN 15104 |
Nitrogen N |
CEN 15104 |
Hydrogen H |
CEN 15104 |
gross calorific value at constant volume Hov |
CEN 14918 |
net calorific value at constant pressure Hup |
CEN 14918 |
fusibility of ash, oxidising atmosphere |
Ash by 550°C |
shrinkage starting temperature SST |
15370-1 |
deformation temperature DT |
CEN 15370-1 |
sphere temperature ST |
|
hemisphere temperature HT |
CEN 15370-1 |
flow temperature FT |
CEN 15370-1 |
Fluorine F |
ISO 11724 |
Chlorine Cl |
CEN 15289 |
decomposition method |
CEN 15297 |
Aluminium Al |
CEN 15297 |
Antimony Sb |
CEN 15297 |
Arsenic As |
CEN 15297 |
Lead Pb |
CEN 15297 |
Cadmium Cd |
CEN 15297 |
Chromium Cr |
CEN 15297 |
Iron Fe |
CEN 15297 |
Cobalt Co |
CEN 15297 |
Copper Cu |
CEN 15297 |
Mangannese Mn |
CEN 15297 |
Nickel Ni |
CEN 15297 |
Quecksilber Hg |
CEN 15297 |
Thallium Tl |
CEN 15297 |
Vanadium V |
CEN 15297 |
Zinc Zn |
CEN 15297 |
Tin Sn |
CEN 15297 |
EOX, extractable organic halogen |
DIN 38414-S17 |
Ash major elements |
Ash by 550°C |
SiO2 |
CEN 15290 |
Al2O3 |
CEN 15290 |
Fe2O3 |
CEN 15290 |
CaO |
CEN 15290 |
MgO |
CEN 15290 |
Na2O |
CEN 15290 |
K2O |
CEN 15290 |
TiO2 |
CEN 15290 |
SO3 |
CEN 15290 |
P2O5 |
CEN 15290 |
MnO2 |
CEN 15290 |
BaO |
CEN 15290 |
SrO |
CEN 15290 |
particle density |
EN 15150 |
bulk density (analog, lower volume <5L) |
EN 15103 |
abrasion <3,15 mm (Ligno-Test) |
LIGNO Test |
mecanical durability | CEN 15210 |